INEOS PP L10G-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M62hFR_INEOS-PP-L10G-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| L10G-00 is a medium melt flow rate, barefoot impact copolymer polypropylene designed for injection molding, compounding applications, and consumer products. Characteristics of this grade include high impact resistance and high flexural modulus. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.906 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.7 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 26.7 | MPa | |
| Break | 15.4 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 250 | % | |
| Flexural Modulus - 1% Secant | 1190 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 43 | J/m | |
| 23°C | 130 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 4.40 | kJ/m² | |
| 23°C | 12.9 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Ductile | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 92.8 | °C | |
| 1.8 MPa, Unannealed | 51.7 | °C | |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 83 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2800B-60A HF | RTP Company | TPV | RTP |
| TUFNYL® SFM 24 BLACK | SRF Ltd. | Nylon 6 | TUFNYL® |
| Hifax BC 72 G | LyondellBasell Industries | PP Copolymer | Hifax |
| LEXAN™ ML2910 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Karina BLACK PVC COMPOUND -E 828-48/ 27-Y-RT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |