Generic ABS - Glass Fiber
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M5ivW9_Generic-ABS---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.07 - 1.37 | g/cm³ | ASTM D792 |
| 23°C | 1.10 - 1.33 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 220°C/10.0 kg | 2.5 - 12 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 0.20 - 19 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 5.25 - 13.4 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.050 - 0.36 | % | ASTM D955 |
| Transverse flow : 23°C | 0.38 - 0.70 | % | ASTM D955 |
| 23°C | 0.18 - 0.40 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.050 - 0.35 | % | ASTM D570 |
| 23°C, 24 hr | 0.030 - 0.45 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 - 0.21 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 98 - 126 | ASTM D785 | |
| 23°C | 109 - 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 58.0 - 9830 | MPa | ASTM D638 |
| 23°C | 3420 - 8040 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 40.8 - 99.4 | MPa | ASTM D638 |
| Yield, 23°C | 43.0 - 114 | MPa | ISO 527-2 |
| Fracture, 23°C | 40.5 - 98.5 | MPa | ASTM D638 |
| Fracture, 23°C | 41.5 - 102 | MPa | ISO 527-2 |
| 23°C | 41.4 - 105 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.0 - 3.6 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 5.3 | % | ASTM D638 |
| Fracture, 23°C | 1.7 - 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2800 - 8530 | MPa | ASTM D790 |
| 23°C | 3200 - 8010 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 60.4 - 161 | MPa | ASTM D790 |
| 23°C | 59.0 - 157 | MPa | ISO 178 |
| Yield, 23°C | 64.8 - 142 | MPa | ASTM D790 |
| Fracture, 23°C | 63.3 - 132 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 - 9.2 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 7.0 - 50 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 47 - 110 | J/m | ASTM D256 |
| 23°C | 4.9 - 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 230 - 410 | J/m | ASTM D256 |
| 23°C | 15 - 24 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 4.80 - 15.3 | J | ASTM D3763 |
| 23°C | 1.60 - 3.34 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 96.3 - 114 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 99.3 - 105 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 89.2 - 108 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.8 - 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 99.1 - 116 | °C | ASTM D1525 |
| -- | 98.8 - 111 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 1.3E-5 - 5.5E-5 | cm/cm/°C | ASTM D696 |
| Flow | 2.2E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.3E-5 - 8.1E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 60.0 - 75.0 | °C | UL 746 |
| RTI Imp | 60.0 - 75.0 | °C | UL 746 |
| RTI | 60.0 - 75.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 50 - 2.5E+15 | ohms | ASTM D257 |
| -- | 1.0E+13 - 2.5E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 1.0E+2 - 1.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+13 - 2.5E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 16 - 19 | kV/mm | ASTM D149 |
| 23°C | 30 - 37 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 398 - 600 | V | IEC 60112 |
| Hot-wire Ignition (HWI) | 120 | sec | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 550 - 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.0 - 87.0 | °C | |
| Drying Time | 2.0 - 9.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Suggested Max Moisture | 0.048 - 0.10 | % | |
| Suggested Shot Size | 55 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 193 - 254 | °C | |
| Middle Temperature | 214 - 238 | °C | |
| Front Temperature | 204 - 271 | °C | |
| Nozzle Temperature | 209 - 245 | °C | |
| Processing (Melt) Temp | 213 - 261 | °C | |
| Mold Temperature | 53.6 - 80.7 | °C | |
| Injection Pressure | 73.4 - 105 | MPa | |
| Back Pressure | 0.150 - 2.01 | MPa | |
| Screw Speed | 45 - 75 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP GP3103 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Network Polymers HDPE 50 2053 | Network Polymers, Inc. | HDPE | Network Polymers HDPE |
| Adell Polyamide AH-18 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| OmniPro™ CPP TF10 | OMNI Plastics, LLC | PP Copolymer | OmniPro™ |
| SCHULABLEND® (PC/ABS) M/MB 6101 GF20 | A. Schulman Europe | PC+ABS | SCHULABLEND® |