TECHNYL® A 218G1 V30 BLACK 34 N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M4pC2O_TECHNYL-A-218G1-V30-BLACK-34-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, reinforced with 30% of glass fibre, for injection moulding This grade shows an improved retention of properties after long term ageing in automotive cooling liquids. For 700 hours' ageing at 132 °C and pressure of 2 bars in water glycol envi |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.80 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10000 | 7500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 195 | 140 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 3.0 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | 9200 | 6400 | MPa | ISO 178 |
| Flexural Stress | 280 | 185 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ||||
| -- | 85 | 100 | kJ/m² | ISO 179/1eU |
| -- 1 | 55 | -- | kJ/m² | ISO 179/1fU |
| Notched Izod Impact Strength | 10 | 18 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 2.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 6.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 34 | 29 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.010 | 0.11 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 600 | 600 | V | |
| Solution B | 500 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | After ageing in water/glycol for 200 hr at 135°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M8195 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Pro-fax PI674 | INDELPRO, S.A. de C.V. | PP Homopolymer | Pro-fax |
| Delrin® SC655 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Gallonprene® GP520-4007 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Grilamid® L 25 W 40 HL X | EMS-GRIVORY | Nylon 12 | Grilamid® |