Fortron® 1200L1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M3penC_Fortron-1200L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron 1200L1 is an unfilled grade for extrusion applications, which has a high melt viscosity and tensile elongation. The recommended processing conditions are identical to those of our standard unfilled grades. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Viscosity | 430 | Pa·s | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 93 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 88.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 3.0 | % | |
| Break | 15 | % | |
| Flexural Modulus (23°C) | 4100 | MPa | ISO 178 |
| Flexural Stress (23°C) | 141 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 200 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 1 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 275 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 4.0E-5 | cm/cm/°C | |
| Transverse | 4.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 10 kHz | 3.00 | ||
| 1 MHz | 3.00 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E H0100 | Asia Polymer Corporation (APC) | LDPE | Polymer-E |
| Generic Silicone Rubber, LSR - Silica | Generic | Silicone Rubber, LSR | Generic |
| Escorene™ Ultra UL 02133EN2 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Hylex® P1010G40FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| PLEXIGLAS® Sheet Mineral BV | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |