Quadrant EPP Semitron® ESd 490HR
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M3i69I_Quadrant-EPP-Semitron-ESd-490HR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP Semitron® ESd 490HR is a Polyetheretherketone (PEEK) product. It can be processed by compression molding and is available in North America. Typical application: Electrical/Electronic Applications. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.18 | % | |
| Saturation | 1.7 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 105 | ||
| R-Scale | 123 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6480 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 96.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.3 | % | ASTM D638 |
| Flexural Modulus | 6550 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 145 | MPa | ASTM D790 |
| Compressive Modulus | 4140 | MPa | ASTM D695 |
| Compressive Strength (10% Strain) | 179 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.20 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 246 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.596 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 340 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 3 | 1.0E+10 to 1.0E+12 | ohms | Internal Method |
| Dielectric Constant (1 MHz) | 5.33 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.23 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| 3 . | EOS/ESD S11.11 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 4145 | Teknor Apex Company | TPV | Sarlink® TPV |
| Formolon® 24A | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| EPO-TEK® H20E-SLR-HVMX | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hifax CB 1128 A | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| LOXIM 430 01 HB | LOXIM Industries Private Limited | Nylon 66 | LOXIM |