Sipolprene® 35150 B
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | SIPOL S.p.A |
| Trademark: | Sipolprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M3IUsU_Sipolprene-35150-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sipolprene® 35150 B (black color version in dry blend) is a block ether ester thermoplastic elastomer (TPC-ET), developed and manufactured by Sipol, with a nominal hardness of Shore D 36, a low modulus, and a rheological behaviour that makes it suitable for injection moulding and extrusion processing. It has been specifically developed with a low melting point which makes it suitable for blending with PVC to make soft compounds plasticizer free. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Water Absorption 1(23°C, 24 hr) | 0.90 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 36 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 28.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 600 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 40.0 | MPa | ASTM D790, ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 100 | kN/m | ASTM D1004 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 105 | °C | ISO 306/A50, ASTM D1525 2 |
| Peak Melting Temperature | 150 | °C | ASTM D3418, ISO 3146 |
| Note Message | |
|---|---|
| 1 . | Immersion |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP NPPH2GF3.2-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| FHR Polypropylene AP5325-HS | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| HiFill® PA6/6 GF33 HR L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Hostalen PP H2150-RC | LyondellBasell Industries | PP Homopolymer | Hostalen |
| LG ASA LI970 | LG Chem Ltd. | ASA | LG ASA |