Kepital® F30-34
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M34tf7_Kepital-F30-34.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A very easy-flowing grade for injection molding of complicated and of thin-walled parts. It has improved on mold deposit. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 36 | g/10 min | ASTM D1238 |
| -- | 36 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.00 mm | 2.0 | % | ASTM D955 |
| 3.00 mm | 2.0 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.22 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 62.0 | MPa | ASTM D638 |
| Yield, 23°C | 65.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 40 | % | ASTM D638 |
| Break, 23°C | 22 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2650 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| 23°C | 91.0 | MPa | ASTM D790 |
| 23°C | 90.0 | MPa | ISO 178 |
| Shear Strength (2.00 mm) | 55.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 158 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 103 | °C | ISO 75-2/A |
| Melting Temperature | 165 | °C | |
| CLTE - Flow (20 to 80°C) | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 19 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 7.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP TPO TPO-185 Black | Washington Penn Plastic Co. Inc. | TPO | WPP TPO |
| UNISOFT ADHESION™ AD-45A-NT-5-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT ADHESION™ |
| ESTACARB 0820 GF V0-5V | Cossa Polimeri S.r.l. | PC | ESTACARB |
| KW Plastics KWR102CA17 | KW Plastics | HDPE | KW Plastics |
| Vydyne® ECO315J BK0707 | Ascend Performance Materials Operations LLC | Nylon 66/6 | Vydyne® |