Tarnamid® T- 27 CFHI
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M1w1Gh_Tarnamid-T--27-CFHI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is reinforced polyamide 6 compound, heat stabilised and impact modified., good conductive and electrostatic properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.11 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 35.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 1.4 | -- | % | |
| Flow : 2.00 mm | 1.1 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 120 | 90.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5500 | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 90.0 | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 6.0 | 13 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4000 | 3300 | MPa | ISO 178 |
| Flexural Stress 2 | 100 | 75.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 11 | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 80 | 120 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 12 | 15 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 170 | 170 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 180 | 165 | °C | ISO 306/B |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.9E-4 | -- | cm/cm/°C | |
| Limit of Temperature - a few hours operation | 180 | -- | °C | |
| Temperature Index - 20000 hr | 120 | -- | °C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | + | -- | FMVSS 302 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA6, MHRZ, 14-050, CF8 | -- | ISO 1874 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+10 | -- | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLOX 111 G6 DX0 | Taro Plast S.p.A. | PET | TAROLOX |
| DOW鈩?Adhesive Film (DAF) 780 | The Dow Chemical Company | Polyolefin, Unspecified | DOW鈩?Adhesive Film (DAF) |
| VAMPALLOY 0023 V0 E | Vamp Tech | PC+ABS | VAMPALLOY |
| UNITIKA Nylon 66 BV2120G30 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| ALTECH® PP-H B 4920/500 MR20 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |