Nypol® PA A3 G50 HS RH PRTA012 NR439
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M1g4SN_Nypol-PA-A3-G50-HS-RH-PRTA012-NR439.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in black color reinforced with 50% of fiberglass, heat stabilized, resistance to hydrolysis and great superficial completion. Good set of thermal properties, electrical and mechanical. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.56 to 1.57 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium, 2.00 mm) | 1.1 | -- | % | ASTM D570 |
| Ash Content | 48 to 52 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 250 | 200 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | 3.4 | % | ASTM D638 |
| Flexural Modulus | 16800 | 12900 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 19 | 16 | kJ/m² | ISO 179 |
| Notched Izod Impact (Area) (23°C) | 18.0 | 20.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact (Area) (-30°C) | 15.0 | 15.0 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 257 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 285 to 295 | °C | |
| Mold Temperature | 100 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® LD 19009 | Plastic Solutions, Inc. | LDPE | PrimaFlex® |
| Texin® RxT70A | Covestro - PUR | TPU-Polyether | Texin® |
| XENOY™ 6370 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |
| G-PAEK™ G-COAT 501 | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| K-Bin Rigid PVC KB-5020 | K-Bin, Inc. | PVC, Unspecified | K-Bin Rigid PVC |