ALCUDIA® LDPE 2303-F
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M1GwTb_ALCUDIA-LDPE-2303-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 2303F is a low density polyethylene grade, produced by high pressure tubular technology, suitable for blown or cast film applications. This material offers easy processability and good balance of mechanical and optical properties. It does not contain any additives. TYPICAL APPLICATIONS
Recommended melt temperature range from 180 to 210°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.40 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 200 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 200 µm, blown film | 9.00 | MPa | ISO 527-3 |
| TD : Yield, 200 µm, blown film | 9.00 | MPa | ISO 527-3 |
| MD : Fracture, 200 µm, blown film | 21.0 | MPa | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 200 µm, blown film | 480 | % | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 500 | % | ISO 527-3 |
| Dart Drop Impact (200 µm, blown film) | 900 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 200 µm, blown film | 5.8 | N | ISO 6383-2 |
| TD : 200 µm, blown film | 9.3 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45 °, 200 µm, blown film) | 50 | ASTM D2457 | |
| Haze (200 µm, blown film) | 12 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 200 µm thickness film, blow up ratio 2.25:1, frost line height 60 cm. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LAP274 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| TOTAL Polypropylene PPC 7642 | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| ACCUTECH™ HP0334T30L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| AIE PA66 60G6F | Asia International Enterprise (Hong Kong) Limited | Nylon 66 | AIE PA66 |
| Dryflex® A2 602601 | ELASTO | SEBS | Dryflex® |