Generic PBT+PET - Glass Fiber
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M0yfg0_Generic-PBT-PET---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PBT+PET - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.40 - 1.73 | g/cm³ | ASTM D792 |
| 23°C | 1.42 - 1.68 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 - 0.80 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (265°C/2.16 kg) | 17 - 22 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 12.9 - 18.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.34 - 1.3 | % | ASTM D955 |
| Transverse flow : 23°C | 0.74 - 0.82 | % | ASTM D955 |
| 23°C | 0.20 - 1.1 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.050 - 0.31 | % | ISO 62 |
| Saturated, 23°C | 0.30 - 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.055 - 0.21 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) (23°C) | 80.0 - 95.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 110 - 120 | ASTM D785 | |
| Ball Indentation Hardness | 110 - 252 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 5000 - 10800 | MPa | ASTM D638 |
| 23°C | 5790 - 16700 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 89.3 - 141 | MPa | ASTM D638 |
| Yield, 23°C | 87.5 - 175 | MPa | ISO 527-2 |
| Fracture, 23°C | 50.0 - 141 | MPa | ASTM D638 |
| Fracture, 23°C | 97.5 - 160 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 1.0 - 3.0 | % | ASTM D638 |
| Yield, 23°C | 1.0 - 4.5 | % | ISO 527-2 |
| Fracture, 23°C | 1.7 - 3.9 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 3.2 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 11900 | MPa | ISO 899-1 |
| 1000 hr | 10600 | MPa | ISO 899-1 |
| Flexural Modulus | |||
| 23°C | 4460 - 13900 | MPa | ASTM D790 |
| 23°C | 5060 - 18100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 89.2 - 208 | MPa | ASTM D790 |
| 23°C | 162 - 260 | MPa | ISO 178 |
| Yield, 23°C | 163 - 173 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.9 - 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 24 - 70 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 34 - 100 | J/m | ASTM D256 |
| 23°C | 8.9 - 10 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 270 - 830 | J/m | ASTM D256 |
| 23°C | 25 - 61 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 6.00 - 8.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 199 - 221 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 214 - 225 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 158 - 211 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 172 - 210 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 185 - 221 | °C | ASTM D1525 |
| -- | 200 - 215 | °C | ISO 306 |
| Melting Temperature | 237 - 240 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 2.1E-5 - 4.5E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.9E-5 - 5.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 5.4E-5 - 8.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 5.9E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.25 - 0.27 | W/m/K | ISO 8302 |
| RTI Elec | 75.0 - 140 | °C | UL 746 |
| RTI Imp | 75.0 - 125 | °C | UL 746 |
| RTI | 75.0 - 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 - 1.1E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+12 - 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 19 - 24 | kV/mm | ASTM D149 |
| 23°C | 15 - 34 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 3.76 | IEC 60250 | |
| Dissipation Factor (23°C) | 8.0E-4 - 0.017 | IEC 60250 | |
| Comparative Tracking Index | 219 - 303 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 0.0 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 642 - 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 21 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 119 - 130 | °C | |
| Drying Time | 2.9 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 - 0.025 | % | |
| Suggested Shot Size | 50 - 60 | % | |
| Hopper Temperature | 50.0 - 85.0 | °C | |
| Rear Temperature | 230 - 261 | °C | |
| Middle Temperature | 242 - 273 | °C | |
| Front Temperature | 257 - 271 | °C | |
| Nozzle Temperature | 265 - 270 | °C | |
| Processing (Melt) Temp | 260 - 273 | °C | |
| Mold Temperature | 78.2 - 91.4 | °C | |
| Injection Pressure | 79.3 - 81.6 | MPa | |
| Holding Pressure | 2.00 - 80.0 | MPa | |
| Back Pressure | 0.258 - 60.0 | MPa | |
| Screw Speed | 59 - 125 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PBT+PET - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PP HTV145 | Sasol Polymers | PP Homopolymer | Sasol Polymers PP |
| Selvol™ 165SF | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| TROSIFOL® BG R15 | Kuraray Co., Ltd. | PVB | TROSIFOL® |
| Fainplast PVC ART 20 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Karina GREEN COLOCOR CONCENTRATE 40/ 21-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |