VALOX™ 3607U resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M0ekwD_VALOX-3607U-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COMMERCIAL, VALOX 3607U is a UV-stabilized, flame retardant, injection moulding PBT resin, offering excellent weatherability resistance. Applications: powerplugs |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 16 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 14.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | Internal Method | ||
| Flow | 1.0 to 1.8 | % | |
| Across Flow | 0.90 to 1.8 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.50 | % | |
| Equilibrium, 23°C, 50% RH | 0.14 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 91.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2050 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 50.0 | MPa | |
| Break | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 4.7 | % | |
| Break | 100 | % | |
| Flexural Modulus 2 | 2050 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 30.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 5 | ISO 180/1A | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 110 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 80.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 160 | °C | ISO 306/A50 |
| -- | 125 | °C | ISO 306/B50 |
| -- | 130 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.1E-4 | cm/cm/°C | |
| Transverse : 23 to 80°C | 1.1E-4 | cm/cm/°C | |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.83 | ||
| 60 Hz | 2.83 | ||
| 1 MHz | 2.71 | ||
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 2.8E-3 | ||
| 60 Hz | 2.8E-3 | ||
| 1 MHz | 0.013 | ||
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-1 | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 245 to 265 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 430 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Borealis PP PP4874 | Borealis AG | PP, Unspecified | Borealis PP |
| Braskem PP TI2900C | Braskem America Inc. | PP, High Crystal | Braskem PP |
| Ferro PP LPP30BC11BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Epocast 1626 A/B | Huntsman Advanced Materials | Epoxy | Epocast |