Sumikon® FM-TK217A
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | M0Qdwo_SumikonFMTK217A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® FM-XTK217A is a Heat dissipative thermoplastic molding compounds, Non-electrical insulative (7W/mk) glass fiber and Heat dissipative filler filled Poly phenylene sulfide molding compound. This grade is official registered UL with V-0 (t=1.0). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.96 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow | 0.20 | % | Internal method |
| Transverse flow | 0.40 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 75.0 | MPa | ASTM D638 |
| Flexural Modulus | 26000 | MPa | ASTM D790 |
| Flexural Strength | 164 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | 3.0 | W/m/K | |
| Coefficient of Linear Thermal Expansion | TMA | ||
| MD | 21 | ppm | TMA |
| TD | 24 | ppm | TMA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 10 | ohms·cm | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.0 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4565A | Teknor Apex Company | TPE | Telcar® |
| Alathon® L5005V | LyondellBasell Industries | HDPE | Alathon® |
| Daplen™ EE168AIB | Borealis AG | PP, Unspecified | Daplen™ |
| KOPA® KN332G35VF | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Thermec N™ 4314R30H | Technical Polymers, LLC | PPA | Thermec N™ |