MAJORIS AFR261 - 8229
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LzmVVw_MAJORIS-AFR261---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AFR261 - 8229 is a low halogen flame retardant compound UL 94 V2, intended for blow moulding extrusion and profiles. The product is available in natural but other colours can be provided on request AFR261 - 8229 produce low level of toxicity and low smoke density in the case of a fire. APPLICATIONS AFR261 - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts (conform 2002/95/EC, RoHS directive).
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1850 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1680 | MPa | ISO 178 |
| Flexural Stress | 34.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 117 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 61.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Horizontal Flame Test 2 | C2B |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 200 | °C | |
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 190 | °C | |
| Cylinder Zone 3 Temp. | 180 to 190 | °C | |
| Cylinder Zone 5 Temp. | 180 to 190 | °C | |
| Melt Temperature | 200 | °C | |
| Die Temperature | 200 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | Test Method: D45 1333 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® AS10BK6603 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Altuglas® HFI-7 Frosted 18 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Fainplast PVC PK 8050/N | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Ebalta GM 984-2 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| LNP™ THERMOCOMP™ PF005S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |