BCC Resins BC 100 Thick
| Category: | EA , Ethylene Acrylate Copolymer |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LzcotK_BCC-Resins-BC-100-Thick.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BC100 Thick is the slow and thickest member of the BCC Products line of cyanoacrylate adhesive. Excellent for gap filling the BC100 Thick has a 30 second fixture time allowing for the material to fill voids and bonding areas. Bonds well to a variety of substrates and materials, formulated especially to plastics, metals and elastomers. Perfect for bonding rough and irregular surfaces and applications requiring up to 15 seconds of alignment and work time. BONDING SCHEDULES Steel: 25-35 seconds ABS: 10-30 seconds Neoprene: <5 seconds PVC: 10-30 seconds Aluminum: 10-20 seconds Phenolics: 10-15 seconds Polycarbonate: 15-20 seconds Nitrile Rubber: 5-7 seconds |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shear Strength | |||
| -- 1 | 6.00 to 9.00 | MPa | ASTM D1002 |
| -- 2 | 10.0 to 15.0 | MPa | ASTM D1002 |
| -- 3 | 5.00 to 10.0 | MPa | ASTM D1002 |
| -- | 15.0 to 22.0 | MPa | ASTM D732 |
| -- 4 | 8.00 to 14.0 | MPa | ASTM D1002 |
| -- 5 | 10.0 to 15.0 | MPa | ASTM D1002 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 125 | °C | ASTM E228 |
| Melting Temperature | 160 to 170 | °C | |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.10 | W/m/K | ASTM C177 |
| Service Temperature | -60 to 80 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gap Filling | 450.0 | µm |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Mix Viscosity 6(25°C) | 1500 | cP | ASTM D2393 |
| Post Cure Time | 24 | hr |
| Note Message | |
|---|---|
| 1 . | PVC |
| 2 . | Acrylics |
| 3 . | Polycarbonate |
| 4 . | ABS |
| 5 . | Neoprene Rubber |
| 6 . | Brookfield LVF, Spindle 1-60 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® DP1694/75 | API SpA | SEBS | megol® |
| Spartech PS SP-2050 | Spartech Plastics | PS (HIPS) | Spartech |
| WACKER SilGel® 613 A/B | Wacker Chemie AG | Silicone | WACKER SilGel® |
| Delta IPP 2508 | Delta Polymers | PP Copolymer | Delta |
| INEOS PP 100-GA09 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |