Niretan B C1515
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Lz87EO_Niretan-B-C1515.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Poliamide 6 rinforced with a mix glass fibre and mineral filler, for the injection moulding of parts That need good isotropic properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.36 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | 1.2 | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 6.5 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | 80 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1(Yield) | 120 | 60.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 4.0 | 10 | % | ASTM D638 |
| Flexural Modulus 3 | 6000 | 2600 | MPa | ASTM D790 |
| Flexural Strength 4(Break) | 160 | 90.0 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -20°C, 3.20 mm | 30 | 30 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 40 | 60 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 60.0 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 220 | -- | °C | ASTM D3418 |
| CLTE - Flow | 1.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 30 | 25 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.10 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | UL 94 | |
| 3.20 mm | HB | -- | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 Water Absorption @ 24 hrs, ASTM D570, 23°C: 6 to 7% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 225 | RTP Company | Nylon 66 | RTP |
| SABIC® LDPE 2201H1W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| METALCAP PPC373B72 | Polyram Ram-On Industries | PP Copolymer | METALCAP |
| SCLAIR® 19A | NOVA Chemicals | HDPE | SCLAIR® |
| XYRON™ L542V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |