Boda BDF25CP
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ly5sFB_Boda-BDF25CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDF25CP is a low viscosity curative incorporated fluoroelastomer copolymer. BDF25CP is a general purpose grade, well suited for application where good flowability and processing property are required. It can be compounded to meet the major fluoroelastomer specifications. BDF25CP can be used for compression molding of general purposes. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 25 | MU | |
| Fluorine Content | 66 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 1.80 | N·m | |
| ML 2(177°C) | 0.250 | N·m | |
| t'90 3(177°C) | 1.6 | min | |
| ts2 4(177°C) | 50.0 | sec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 78 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 13.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 180 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 18 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 55T1030S | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PPcompound |
| TECHNO MUH LG5534 | Techno Polymer Co, Ltd. | ABS | TECHNO MUH |
| Sindustris PP GP2101 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| AKROMID® B3 GF 15 black (4002) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| POLYCOMPO PP F107DV | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |