Capran® 75 Datasheet,Nylon 6,Honeywell-SHANGHAI SUSHENG

Message
Capran® is a multipurpose cast nylon 6 film used in food packaging and industrial applications. Its physical properties are evenly distributed for optimum performance giving excellent resistance to flex cracking. It can be processed over a wide temperature range and exhibits outstanding abrasion resistance.

General Information
Features	Low air permeability Radiation disinfection Good disinfection Perforation resistance Impact resistance, good Good cracking resistance Good tear strength Good wear resistance High pressure heating resistance
Uses	Packaging Films Industrial application Food packaging
Forms	Films
Processing Method	Thermoforming

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With Metal-Dynamic	0.35	ASTM D1894
With self-dynamics	0.85	ASTM D1894

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	19	µm
secant modulus			ASTM D882
MD : 19 µm	793	MPa	ASTM D882
TD : 14 µm	862	MPa	ASTM D882
Tensile Strength			ASTM D882
MD : Yield	37.9	MPa	ASTM D882
TD : Yield	37.9	MPa	ASTM D882
MD : Break, 19 µm	122	MPa	ASTM D882
TD : Break, 19 µm	103	MPa	ASTM D882
Tensile Elongation			ASTM D882
MD : Break, 19 µm	340	%	ASTM D882
TD : Break, 19 µm	380	%	ASTM D882
Elmendorf Tear Strength			ASTM D1922
MD : 19 µm	27	g	ASTM D1922
TD : 19 µm	50	g	ASTM D1922
Oxygen Permeability (25°C, 19 µm, 0% RH)	1.6	cm³·mm/m²/atm/24 hr	ASTM D3985
Water Vapor Transmission Rate (19 µm, 38°C, 100% RH)	540	g·mm/m²/atm/24 hr	ASTM F1249

Optical	Nominal Value	Unit	Test Method
Haze	< 10	%	ASTM D1003

Additional Information
Yield: 32702 in²/lbTensile Strength @ Break, ASTM D 882, MD: 14500 to 20000 psiTensile Strength @ Break, ASTM D 882, TD: 13000 to 17000 psiTensile Strength @ Yield, ASTM D 882, MD: 5000 to 6000 psiTensile Strength @ Yield, ASTM D 882, TD: 5000 to 6000 psiElongation @ Break, ASTM 882, MD: 300 to 375%Elongation @ Break, ASTM 882, TD: 350 to 400%Secant Modulus, ASTM D 882, MD: 90000 to 120000 psiSecant Modulus, ASTM D 882, TD: 100000 to 150000 psiGraves Tear (initial), ASTM D 1004, MD: 630 to750 g/milGraves Tear (initial), ASTM D 1004, TD: 630 to750 g/milCoefficient of Friction, ASTM D 1894: 0.70 to 1.0 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.2 to 0.5 vs Metal-DynamicSurface Tension, ASTM D5946, untreated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, treated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: <3.0% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: <3.0% shrinkage

Additional Information

Yield: 32702 in²/lbTensile Strength @ Break, ASTM D 882, MD: 14500 to 20000 psiTensile Strength @ Break, ASTM D 882, TD: 13000 to 17000 psiTensile Strength @ Yield, ASTM D 882, MD: 5000 to 6000 psiTensile Strength @ Yield, ASTM D 882, TD: 5000 to 6000 psiElongation @ Break, ASTM 882, MD: 300 to 375%Elongation @ Break, ASTM 882, TD: 350 to 400%Secant Modulus, ASTM D 882, MD: 90000 to 120000 psiSecant Modulus, ASTM D 882, TD: 100000 to 150000 psiGraves Tear (initial), ASTM D 1004, MD: 630 to750 g/milGraves Tear (initial), ASTM D 1004, TD: 630 to750 g/milCoefficient of Friction, ASTM D 1894: 0.70 to 1.0 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.2 to 0.5 vs Metal-DynamicSurface Tension, ASTM D5946, untreated side: >/= 56 dynes/cmSurface Tension, ASTM D5946, treated side: >50 dynes/cmDimensional Stability, ASTM D1204, MD, 320°F, 5min: <3.0% shrinkageDimensional Stability, ASTM D1204, TD, 320°F, 5min: <3.0% shrinkage

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Honeywell
Trademark:	Capran®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Ly2B70_Capran-75.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP EMI 1060	RTP Company	PBT	RTP
Sinvicomp SFW9002	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Sinvicomp
Bayfit® SA 511 (75 Index)	Covestro - PUR	PUR-MDI	Bayfit®
Kumho ABS HFA 451	Korea Kumho Petrochemical Co., Ltd.	ABS	Kumho ABS
LGG 104	LG Polymers India Pvt. Ltd.	PS (GPPS)	LGG