EPO-TEK® 301-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Lxckby_EPO-TEK-301-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A two component, room temperature curing, optical grade epoxy, designed for optics, medical, and opto-electronic packaging of semiconductor devices, components, and electronics. It is a lower viscosity version of EPO-TEK® 301. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 65.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 5.4E-5 | cm/cm/°C | |
| -- 3 | 1.8E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.517 | ||
| Transmittance | |||
| 400 to 1600 nm | > 96.0 | % | |
| 1600 to 2000 nm | > 92.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 20 | ||
| Part B | Mix Ratio by Weight: 5.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 390 | °C | |
| Die Shear Strength - >5 kg (23°C) | 11.7 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 1.55 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.44 | % | |
| 250°C | 0.84 | % | |
| 300°C | 1.6 | % |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 5 | Clear/Transparent | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part B | 0.868 | g/cm³ | |
| Part A | 1.14 | g/cm³ | |
| Viscosity 7(23°C) | 0.080 to 0.10 | Pa·s | |
| Curing Time (65°C) | 2.0 | hr | |
| Pot Life | 60 to 120 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ||
| Lap Shear Strength (23°C) | 7.58 | MPa | |
| Relative Permittivity (1 kHz) | 4.26 | ||
| Volume Resistivity (23°C) | > 3.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.021 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL GTX™ NX0031 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| Nypol® PA A3 G33 HS UV PRTA011 NR351 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Grilon® CR 9 | EMS-GRIVORY | Nylon 6/12 | Grilon® |
| Hyundai EP PA66 LD430 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| KumhoSunny AES HW601HI | Shanghai KumhoSunny Plastics Co., Ltd. | AES | KumhoSunny AES |