SABIC® PPcompound 9125
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LxA7NY_SABICPPcompound9125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 9125 is a Mineral Filled Modified Polypropylene for aesthetic interior applications. This material combines a high scratch resistance with high stiffness, good impact and high flow. The broad processing window enables application in complex shapes as often found in automotive interior. SABIC® PPcompound 9125 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.90 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, injection molding | 21.0 | MPa | ISO 527-2/1A/50 |
| Fracture, injection molding | 15.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break, Injection Molded) | 20 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1(Injection Molded) | 1800 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/4A | ||
| 0°C, injection molding | 6.0 | kJ/m² | ISO 180/4A |
| 23°C, injection molding | 12 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 106 | °C | ISO 75-2/B |
| CLTE - Flow (-30 to 30°C) | 5.7E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMSTER PF320G2 | Polyram Ram-On Industries | PBT | RAMSTER |
| FORMULA P FIB 3610/L SC | Putsch Kunststoffe GmbH | PP, Unspecified | FORMULA P |
| ISOTHANE® 1685A-E | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |
| LNP™ LUBRICOMP™ RX05049 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ PF00C compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |