KPOL-PP K-PPC 6.0

Category:	PP Impact Copolymer , Polypropylene Impact Copolymer
Manufacturer:	KPOL Chem Co.
Trademark:	KPOL-PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LvqskZ_KPOL-PP-K-PPC-6-0.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Polypropylene Heterophasic Copolymer

Characteristics

The KPOL® resin is a propylene impact copolymer designed for injection molding applications, Excellent Balance of Stiffness and Impact Strength, Contains Nucleating , Good Mold Release.

Applications

Injection Molding, of thick parts, containers, closures, battery cases. SPC in general.

Superior Drop Impact at Refrigeration Temperature, Very High Flexural Modulus. Also is suitable for technical components: toys, sports, equipment, leisure goods, automotive, pallets, crates and pails.

General Information
Additive	Antioxidant Nucleating Agent
Features	Antioxidant Good Impact Resistance Good Mold Release Good Stiffness Impact Copolymer Low Temperature Resistant Nucleated
Uses	Automotive Applications Battery Cases Closures Containers Crates Pallets Sporting Goods Thick-walled Parts Toys
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.902	g/cm³	ASTM D1505
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	6.0	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	82		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield)	33.0	MPa	ASTM D638
Tensile Elongation ²(Break)	8.5	%	ASTM D638
Flexural Modulus - 1% Secant	1450	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (-20°C)	180	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	88.0	°C	ASTM D648
Vicat Softening Temperature	92.0	°C	ASTM D1525 ³

Note Message
1 .	Type IV, 50 mm/min
2 .	Type IV, 50 mm/min
3 .	Rate A (50°C/h), Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Nypol® PA A3 G33 HS NTLA013 NR307	Petropol Industry and Trade of Polymers LTDA	Nylon 66	Nypol® PA
Devcon Stainless Steel Putty (ST)	Devcon	Epoxy	Devcon
POLYFORT® FPP 1640	A. Schulman Inc.	PP, Unspecified	POLYFORT®
TABOREN® PH 89 T 20-075	SILON s.r.o.	PP Homopolymer	TABOREN®
LEXAN™ EXL1132 resin	SABIC Innovative Plastics	PC	LEXAN™