LNP™ THERMOCOMP™ PF007S compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LvNLwN_LNP-THERMOCOMP-PF007S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP PF007S is a compound based on Nylon 6 resin containing 35% Glass Fiber. Added feature of this material is: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound PF007S Product reorder name: PF007S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 1.0 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11900 | MPa | ASTM D638 |
| -- | 11500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 167 | MPa | ASTM D638 |
| Break | 162 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.0 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 10600 | MPa | ASTM D790 |
| -- 5 | 10300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 211 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 236 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 80 | J/m | ASTM D256 |
| 23°C 7 | 7.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 720 | J/m | ASTM D4812 |
| 23°C 8 | 43 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 9.16 | J | ASTM D3763 |
| -- | 2.32 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 218 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 217 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 209 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 205 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.0E-6 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil CV1-2960 | NuSil Technology | Silicone | NuSil |
| Kingfa PC-S923 | Kingfa | PC Alloy | Kingfa |
| HiFill® PPSU 4000 BK | Techmer Engineered Solutions | PPSU | HiFill® |
| LNP™ STAT-KON™ WX06322 compound | SABIC Innovative Plastics Asia Pacific | PBT | LNP™ STAT-KON™ |
| Monprene® RG-18280 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |