KumhoSunny PA/PPE HAP8720C
| Category: | Nylon+PPE , Polyamide + PPE |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PA/PPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LvIg7m_KumhoSunny-PA-PPE-HAP8720C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HAP8720C is a conductive PA/PPE alloy especially designed for in- or on-line painted bodypanels and fenders in particular. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage (23°C) | 1.1 to 1.5 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 10 | % | ISO 527-2/50 |
| Flexural Modulus 1(64.0 mm) | 2250 | MPa | ISO 178 |
| Flexural Stress 2(64.0 mm) | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179 | ||
| -30°C | 9.9 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength 4 | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength 5 | ISO 180 | ||
| -30°C | 7.6 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Unnotched Izod Impact Strength 6 | ISO 180 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed | 190 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 9.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+5 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 99.0 to 105 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 275 to 300 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Condition: 4 J |
| 4 . | Condition: 4 J |
| 5 . | Condition: 5.5 J |
| 6 . | Condition: 5.5 J |
| 7 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resinoid 7005 | Resinoid Engineering Corporation | Phenolic | Resinoid |
| Heramid® A GRI 7645 ECP1904 | Radici Plastics | Nylon 66 | Heramid® |
| IROGRAN® A 85 P 4350 | Huntsman Corporation | TPU-Polyether | IROGRAN® |
| IROSTIC® S 6148 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |
| POLYfill PP HGX500707 | Polykemi AB | PP, Unspecified | POLYfill |