Grivory® HT2C-3X black 9833
| Category: | Nylon 6T/66 , Polyamide 6T/66 Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grivory® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LuunfI_Grivory-HT2C-3X-black-9833.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grivory® HT2C-3X black 9833 is a Polyamide 6T/66 Copolymer (Nylon 6T/66) material filled with 30% carbon fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grivory® HT2C-3X black 9833 are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 300 | 290 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 24500 | 24000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 275 | 265 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | 2.0 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 7.0 | kJ/m² | |
| 23°C | 8.0 | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 50 | kJ/m² | |
| 23°C | 55 | 55 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 290 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 245 | -- | °C | ISO 75-2/C |
| Maximum Use Temperature | Internal Method | |||
| Long Term | 140 | -- | °C | |
| Short Term | 240 | -- | °C |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA 6T/66, MH, 14-250, CF30 | -- | ISO 1874 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 310 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.5E-5 | -- | cm/cm/°C | |
| Transverse | 7.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+2 | ohms | IEC 60093 |
| Volume Resistivity | 5.0E+3 | 5.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® BGF40 BK | Ravago Group | Nylon 6 | Ravamid® |
| Shuman ABS 780H | Shuman Plastics, Inc. | ABS | Shuman ABS |
| TechnoPet 3520 | TechnoCompound GmbH | PET | TechnoPet |
| Fainplast PVC MPH 57/Y | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| POLYFLAM® RPP 2120 | A. Schulman Europe | PP Homopolymer | POLYFLAM® |