Vydyne® R530H BK0713
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LuDoyI_VydyneR530HBK0713.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| R530H BK0713 is a black, 30% glass-fiber reinforced, PA66 that is heat stabilized. R530H BK0713 is bromine-free and is optimized for excellent laser welding and marking. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.37 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Lateral flow : 23°C, 2.00mm | 0.90 | -- | % | ISO 294-4 |
| Traffic : 23°C, 2.00mm | 0.40 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | ISO 62 |
| Balance, 50% RH | 1.9 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10000 | 7400 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 195 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9600 | 6000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 270 | 190 | MPa | ISO 178 |
| Poisson's Ratio (23°C) | 0.40 | -- | ISO 527 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | 11 | kJ/m² | ISO 179 |
| 23°C | 11 | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 65 | 80 | kJ/m² | ISO 179 |
| 23°C | 75 | 85 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180 | |||
| -30°C | 10 | 11 | kJ/m² | ISO 180 |
| 23°C | 12 | 13 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00mm | 2.2E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C, 2.00mm | 1.1E-4 | -- | cm/cm/°C | ISO 11359-2 |
| RTI Elec | UL 746 | |||
| 0.75 mm | 140 | -- | °C | UL 746 |
| 1.5 mm | 140 | -- | °C | UL 746 |
| 3.0 mm | 140 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 0.75 mm | 120 | -- | °C | UL 746 |
| 1.5 mm | 120 | -- | °C | UL 746 |
| 3.0 mm | 120 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 0.75 mm | 125 | -- | °C | UL 746 |
| 1.5 mm | 140 | -- | °C | UL 746 |
| 3.0 mm | 140 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity (3.00 mm) | 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength (1.00 mm) | 20 | -- | kV/mm | IEC 60243 |
| Arc Resistance (3.00 mm) | PLC 6 | -- | ASTM D495 | |
| Comparative Tracking Index (3.00 mm) | 250 - 399 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.75 mm | PLC 0 | -- | UL 746 | |
| 1.5 mm | PLC 0 | -- | UL 746 | |
| 3.0 mm | PLC 0 | -- | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 1 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.75 mm | PLC 4 | -- | UL 746 | |
| 1.5 mm | PLC 3 | -- | UL 746 | |
| 3.0 mm | PLC 4 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.75 mm | HB | -- | UL 94 | |
| 1.5 mm | HB | -- | UL 94 | |
| 3.0 mm | HB | -- | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.75 mm | 675 | -- | °C | IEC 60695-2-12 |
| 1.5 mm | 675 | -- | °C | IEC 60695-2-12 |
| 3.0 mm | 675 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.75 mm | 700 | -- | °C | IEC 60695-2-13 |
| 1.5 mm | 700 | -- | °C | IEC 60695-2-13 |
| 3.0 mm | 700 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 - 310 | °C | |
| Middle Temperature | 280 - 310 | °C | |
| Front Temperature | 280 - 310 | °C | |
| Nozzle Temperature | 280 - 310 | °C | |
| Processing (Melt) Temp | 285 - 305 | °C | |
| Mold Temperature | 65 - 95 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoTek KM6130 | KMI Group Inc. | PBT | PrimoTek |
| TEKAMID™ TB120G15 | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| Cosmic Epoxy EH71 | Cosmic Plastics, Inc. | Epoxy | Cosmic Epoxy |
| Plexiglas® 7H | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| Latigray 82-02 CX/80 | LATI S.p.A. | Nylon 12 | Latigray |