| LEXAN LUX2289 resin is an injection molding grade with high light reflectance and UV stabilized |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.34 | g/cm³ | ASTM D792 |
| -- | 1.31 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 17 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 60.0 | MPa | ASTM D638 |
| Yield | 61.0 | MPa | ISO 527-2/50 |
| Fracture 2 | 61.0 | MPa | ASTM D638 |
| Fracture | 62.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 4 | 120 | % | ASTM D638 |
| Flexural Modulus | |||
| 50.0mm span 5 | 2670 | MPa | ASTM D790 |
| -- | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 70.0 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 98.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7 | ISO 179/1eA | ||
| -30°C | 180 | kJ/m² | ISO 179/1eA |
| 23°C | 180 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 8 | ISO 179/1eU | ||
| -30°C | 140 | kJ/m² | ISO 179/1eU |
| 23°C | 140 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| -30°C | 170 | J/m | ASTM D256 |
| 23°C | 650 | J/m | ASTM D256 |
| -30°C 9 | 13 | kJ/m² | ISO 180/1A |
| 23°C 10 | 52 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D4812 |
| -30°C 11 | 160 | kJ/m² | ISO 180/1U |
| 23°C 12 | 170 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 69.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 136 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 124 | °C | ASTM D648 |
| 1.8 MPa, annealed 13 | 123 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ASTM D1525 14 |
| -- | 144 | °C | ISO 306/A50 |
| -- | 145 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 260 - 282 | °C | |
| Middle Temperature | 271 - 293 | °C | |
| Front Temperature | 282 - 304 | °C | |
| Nozzle Temperature | 277 - 299 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 71.0 - 93.0 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*3 sp=62mm |
| 8 . | 80*10*3 sp=62mm |
| 9 . | 80*10*3 |
| 10 . | 80*10*3 |
| 11 . | 80*10*3 |
| 12 . | 80*10*4 |
| 13 . | 2 hr, 120°C |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 402 M NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| ACCUTECH™ HP0336C20L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| EnCom PC-ABS 7000 | EnCom, Inc. | PC+ABS | EnCom |
| Hylon® N1233HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| SECCO GPPS-123 | Shanghai SECCO Petrochemical Co., Ltd | PS (GPPS) | SECCO |