Blendfor® A 4000/V0 NERO
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Blendfor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LrTT9V_Blendfor-A-4000-V0-NERO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant PC/ABS grade, excellent impact resistance and good fluidity |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.55 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 45.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 2100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 106 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Needle Flame Test | Pass | IEC 60695-11-5 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Ignition Temperature | 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 210 | °C | |
| Front Temperature | 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 1022H | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| megol® TA 80 | API SpA | SEBS | megol® |
| Daelim Po1y® 5502HS | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| FRIANYL® A3 GF20 V2XI | Nilit Plastics | Nylon 66 | FRIANYL® |
| Honeywell PMP R2000 | Honeywell | PMP | Honeywell PMP |