LNP™ THERMOCOMP™ RF006L compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LrMETF_LNPTHERMOCOMPRF006Lcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF006L is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible. Also known as: LNP* THERMOCOMP* Compound RF-1006 LE Product reorder name: RF006L |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.59 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 10500 | MPa | ASTM D638 |
| Tensile Strength (Break) | 157 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.4 | % | ASTM D638 |
| Flexural Modulus | 8740 | MPa | ASTM D790 |
| Flexural Strength | 221 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 750 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 246 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 55200 W | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Nylene® 474 | Custom Resins Group | Nylon 6 | Nylene® |
| Amilan® CM3004G-30 | Toray Resin Company | Nylon 66 | Amilan® |
| Di-Pak™ R-4528/17 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Lucent PC PC/PBT-1231 | Lucent Polymers, Inc. | PC+PBT | Lucent PC |