Radilon® A RV300L 333 NER
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LqoahI_Radilon-A-RV300L-333-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 30% glass fiber reinforced injection moulding grade. Lubricated. Black colour. Suitable for parts requiring high stiffness and easier flow. ISO 1043 : PA66 GF30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 7.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9600 | 6500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 165 | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.4 | 6.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 8500 | 5500 | MPa | ISO 178 |
| Flexural Stress 2 | 255 | 160 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | |
| 23°C | 10 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | -- | kJ/m² | |
| 23°C | 65 | 98 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 235 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 245 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILAC AG15E3 | Formosa Plastics Corporation | ABS | TAIRILAC |
| NORYL™ EM7301HF resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| INSTRUC ABSGF30 | Infinity LTL Engineered Compounds | ABS | INSTRUC |
| Sylvin 6227-83 White 1537 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9077-70 Grey 930 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |