Riblene® FL 34 I
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LqMwoq_RibleneFL34I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FL 34 I is a low density polyethylene (LDPE), additivated with slip and antiblocking agent, suitable for blown film extrusion. Riblene FL 34 I is characterised by a good balance between processability, mechanical and optical properties. Films manufactured by Riblene FL 34 I are easily heat shrinkable. Main Applications Riblene FL 34 I is recommended for general blown film applications, for the production of low gauge film and shrink film and for blend. Riblene FL 34 I thanks its properties is also recommended for the production of high purity film. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Blown Film) | 0.11 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Thickness - Recommended / Available | 25 to 80 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% secant, MD : 40 µm, blown film | 180 | MPa | ISO 527-3 |
| 1% secant, TD : 40 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 23.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 18.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 580 | % | ISO 527-3 |
| Dart Drop Impact 1(40 µm, Blown Film) | 130 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 40.0 µm | 80.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 50.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Melting Temperature | 113 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 70 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 6.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 MS 3 | RTP Company | Acetal (POM) Copolymer | RTP |
| REXtac® APAO RT 27323cs8 | Huntsman Corporation | PAO | REXtac® APAO |
| Ultradur® B 4406 G4 | BASF Corporation | PBT | Ultradur® |
| Gallonprene® GP520-6509 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Forprene® 6NE901D40 | SO.F.TER. SPA | TPV | Forprene® |