Vyncolit® W5016
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LpwKri_Vyncolit-W5016.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit W5016 is a glass fibre and mineral filled phenolic moulding compound with excellent dimensional stability and a very low coefficient of thermal expansion. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.08 | g/cm³ | ISO 1183 |
| Apparent Density | 0.95 to 1.10 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.10 to 0.25 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 0.10 | % | ISO 62 |
| Post Shrinkage | 0.020 to 0.10 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.75 to 0.85 | % | ISO 178 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Type | PF 2 C3 | ||
| Pourability | Excellent |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 28000 to 30000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 to 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.20 to 0.40 | % | ISO 527-2 |
| Flexural Modulus | 23000 to 25000 | MPa | ISO 178 |
| Flexural Stress | 170 to 190 | MPa | ISO 178 |
| Compressive Stress | 340 to 380 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.3 to 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 6.0 to 8.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 190 to 210 | °C | ISO 75-2/Af |
| 8.0 MPa, Unannealed | 160 to 180 | °C | ISO 75-2/C |
| CLTE | TMA | ||
| Flow | 1.2E-5 to 1.6E-5 | cm/cm/°C | |
| Transverse | 1.7E-5 to 2.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Electric Strength | 30 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Insulation Resistance 1 | 1.0E+12 to 1.0E+13 | ohms | IEC 60167 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 4.00 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | Dry |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4670A | Teknor Apex Company | TPE | Telcar® |
| TORZEN® GM3800HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| UNISOFT TPE™ ST-55A-NT-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| NEXT SIGNATURE CAB MG-100 | NEXT Specialty Resins, Inc. | CAB | NEXT SIGNATURE |
| PLUSTEK PA100/PA100NT-N | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |