RapidVac™ VA-1605
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | RapidVac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LooKq0_RapidVac-VA-1605.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VA-1605 is a 60 shore A elastomer formulated for hand-batch processing, vacuum assisted processing or meter mix dispensed. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury. MOCA, or TDI. VA-1605 has excellent green strength for quick demold times. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.13 | g/cm³ | |
| Hardener | 1.13 | g/cm³ | |
| Base Resin | 1.18 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.30 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 52 Mix Ratio by Volume: 50 | ||
| Demold Time | 20 to 40 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.50 | Pa·s | |
| 25°C 2 | 0.85 | Pa·s | |
| 25°C 3 | 0.90 | Pa·s | |
| Curing Time 4 | 25 | hr | |
| Gel Time | 3.0 to 5.0 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 55 to 65 | ASTM D2240 | |
| Tensile Strength | 2.41 | MPa | ASTM D638 |
| Tensile Elongation at Break | 140 | % | ASTM D638 |
| Tear Strength | 7.01 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| 4 . | 24 hours at 77°F + 1 hour at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ GFN3 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Dynaprene® VE5087A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Karina WHITE PVC COMPOUND -E 898-10/137-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1500-0871 | LEHVOSS Group | PSU | LUVOCOM® |
| DAI-EL™ G-901 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |