Hostalen GF 9055 F
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LnvxE5_Hostalen-GF-9055-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen GF 9055F is a high density polyethylene. Films made of Hostalen GF 9055F provide a good barrier against water vapour. It contains antioxidants and is delivered in pellet form. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.954 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 1.8 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Film Thickness - Recommended / Available | 0.8-3.1 mil (20-80 µ) | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 30 µm, blown film | 26.0 | MPa | ISO 527-3 |
| TD : 30 µm, blown film | 50.0 | MPa | ISO 527-3 |
| Tensile Elongation - MD (Broken, 30 µm, blown film) | 430 | % | ISO 527-3 |
| Dart Drop Impact (30 µm, Blown Film) | 30 | g | ASTM D1709 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 30 µm, blown film | 0.80 | N | ISO 6383-2 |
| TD : 30 µm, blown film | 0.20 | N | ISO 6383-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (-30°C) | 30.0 | kJ/m² | ISO 8256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ISO 306/B50 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Staudinger Index | 270 | cm³/g | ISO 1628 |
| Film properties tested using 30 µm thickness blown film extruded at a melt temperature of 190°C and a blow-up ratio of 2.65:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V75M | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| ADMER™ AT2146E | Mitsui Chemicals Europe GmbH | PE, Unspecified | ADMER™ |
| Braskem PP H 214 | Braskem | PP Homopolymer | Braskem PP |
| Karina IVORY PVC COMPOUND 75900-35/1-E-AC (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| NYLOY® MG-1109B | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |