DOWLEX™ 4056.01G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Lngcl8_DOWLEX-4056-01G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™4056.01G is a linear low-density resin used in high-quality blown films. These blown films require a combination of excellent optical properties, tear strength, sealing and excellent processing properties. The low gel content of DOWLEX 4056.01G makes it particularly suitable for composite films and other special packaging applications. The resin contains slip agent and anti-blocking agent. Meet the following regulatory requirements:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.15 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Puncture Energy | Internal method | ||
| 25 µm | 1.70 | J | Internal method |
| 50 µm | 4.30 | J | Internal method |
| Film Puncture Force | Internal method | ||
| 25 µm | 8.60 | N | Internal method |
| 50 µm | 10.8 | N | Internal method |
| Film Puncture Resistance | Internal method | ||
| 25 µm | 103 | J/cm³ | Internal method |
| 50 µm | 124 | J/cm³ | Internal method |
| Dart Drop Impact | ASTM D1709A | ||
| 25 µm | 250 | g | ASTM D1709A |
| 50 µm | 370 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 25 µm | 280 | g | ASTM D1922 |
| MD : 50 µm | 650 | g | ASTM D1922 |
| TD : 25 µm | 420 | g | ASTM D1922 |
| TD : 50 µm | 750 | g | ASTM D1922 |
| Seal Initiation Temperature 2 | Internal method | ||
| 25 µm | 105 | °C | Internal method |
| 50 µm | 105 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 25.0 µm 3 | 81 | ASTM D2457 | |
| 45°, 25.0 µm | 65 | ASTM D2457 | |
| 45°, 25.0 µm 4 | 75 | ASTM D2457 | |
| 45°, 50.0 µm | 64 | ASTM D2457 | |
| 45°, 50.0 µm 5 | 71 | ASTM D2457 | |
| 45°, 50.0 µm 6 | 80 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 25.0 µm 7 | 4.2 | % | ASTM D1003 |
| 25.0 µm | 6.3 | % | ASTM D1003 |
| 25.0 µm 8 | 4.2 | % | ASTM D1003 |
| 50.0 µm | 9.6 | % | ASTM D1003 |
| 50.0 µm 9 | 5.1 | % | ASTM D1003 |
| 50.0 µm 10 | 5.1 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 217 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 熔体温度：217°C 模具直径：200 mm。 放大比：2 比 1 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Realize the temperature of 8.8N/25MM heat sealing strength. Heat seal strength, Topwave HT tester 0.5 S holding pressure, 40 psi pressure, pulling speed (100 mm/s). |
| 3 . | LDPE with 20% |
| 4 . | LDPE with 40% |
| 5 . | LDPE with 40% |
| 6 . | LDPE with 20% |
| 7 . | LDPE with 20% |
| 8 . | LDPE with 40% |
| 9 . | LDPE with 20% |
| 10 . | LDPE with 40% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REVOLVE® N-228 | Matrix Polymers | Plastomer | REVOLVE® |
| TUFLIN™ HS-7094 NT 7 | The Dow Chemical Company | LLDPE | TUFLIN™ |
| CEPLA CT-451 | CEPLA Co., LTD | PP, Unspecified | CEPLA |
| Gallonprene® GP410-5503 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Kynar® 760 | Arkema | PVDF | Kynar® |