RTP 200 H FR
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LnLP1f_RTP-200-H-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Impact - Unreinforced - Flame Retardant - UL94 V-0 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.8 - 2.4 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.80 | % | ASTM D570 |
| Moisture Content | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1930 | MPa | ASTM D638 |
| Tensile Strength | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 320 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 191 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.1 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.70 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.016 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 277 - 299 | °C | |
| Mold Temperature | 65.6 - 107 | °C | |
| Injection Pressure | 68.9 - 124 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® MJ7301C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Nipol® LX855EX1 | Zeon Corporation | Latex | Nipol® |
| Nypol® PA A3 T40 VRD0240 NR373 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Aropol™ 8020 | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Chemraz 661 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |