Order Products : sales@su-jiao.com
Edgetek™ SF-40CF/000
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LmvGV5_Edgetek-SF-40CF-000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.49 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.050 to 0.10 | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 31000 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 200 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 to 3.0 | % | ASTM D638 |
| Flexural Modulus | 27600 | MPa | ASTM D790 |
| Flexural Strength | 296 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 75 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 263 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 304 to 332 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 38GFRH300 | AD majoris | PBT | MALAT |
| POLYLAN AT5500 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| GLS PP ZN09 | GLS Polymers Pvt. Ltd. | PP Homopolymer | GLS PP |
| Leona™ 13G43 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Lupoy® 3030-30 | LG Chem Ltd. | PC | Lupoy® |