LUVOCOM® 3-8097 VP Datasheet,Nylon 6,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®3-8097 VP is a polyamide 6 (nylon 6) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 3-8097 VP are: Conductivity High stiffness high strength Creep resistance Wear-resistant Typical application areas include: Electrical/electronic applications textile/fiber engineering/industrial accessories Automotive Industry

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Heat conduction Rigidity, high High strength Good creep resistance Good wear resistance
Uses	Electrical/Electronic Applications Textile applications Engineering accessories Application in Automobile Field
Appearance	Dark gray

Physical	Nominal Value	Unit	Test Method
Density	1.56	g/cm³	ISO 1183
Molding Shrinkage	0.20 - 0.50	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 1.0	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	16000	MPa	ISO 527-2
Tensile Stress (Break)	140	MPa	ISO 527-2
Tensile Strain (Yield)	1.6	%	ISO 527-2
Flexural Modulus	14000	MPa	ISO 178
Flexural Stress	215	MPa	ISO 178
Flexural Strain at Flexural Strength	2.1	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	210	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+6	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	30	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	90.0	°C	UL 746B
Thermal Conductivity ¹	3.5	W/m/K

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+6	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
A	75.0	°C
B	105	°C
Drying Time
A	10 - 16	hr
B	4.0 - 6.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	250 - 270	°C
Middle Temperature	270 - 290	°C
Front Temperature	280 - 300	°C
Nozzle Temperature	270 - 280	°C
Processing (Melt) Temp	270	°C
Mold Temperature	70.0 - 110	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Note Message
1 .	Hot-Disk, 60x60x3 mm

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	LmPoTT_LUVOCOM-3-8097-VP.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SLOVAMID® 66 GF 10	Plastcom	Nylon 66	SLOVAMID® 66
Surlyn Reflection Series® SURSG201UNM	LTL Color Compounders, Inc.	Nylon 6 Alloy	Surlyn Reflection Series®
CALIBRE™ 301-9	Trinseo	PC	CALIBRE™
Enviramid® N1300STHL BK	Ravago Manufacturing Americas, LLC	Nylon 66	Enviramid®
LNP™ STAT-KON™ DEL22P compound	SABIC Innovative Plastics	PC	LNP™ STAT-KON™