RASCHIG EN 5004/5007
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | RASCHIG GmbH |
| Trademark: | RASCHIG |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LmE3D1_RASCHIG-EN-5004-5007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Mica reinforced moulding compound Low mould shrinkage and post-shrinkage, very good electrical values, outstanding heat resistance, very good pourability. Primary application(s): Car lamp base H-4/H-7 This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.30 to 2.45 | g/cm³ | ISO 1183 |
| Apparent Density | 1.00 to 1.30 | g/cm³ | ISO 60 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | < 0.10 | % | ISO 62 |
| Post Shrinkage 1 | < 0.050 | % | ISO 2577 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 5.00 | MPa | |
| Compression Molding Temperature | 150 to 190 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 to 9000 | MPa | ISO 527-2 |
| Tensile Stress | 30.0 to 50.0 | MPa | ISO 527-2 |
| Flexural Modulus | 20000 to 22000 | MPa | ISO 178 |
| Flexural Stress | 50.0 to 60.0 | MPa | ISO 178 |
| Compressive Stress | 200 to 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 1.5 to 2.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 2.0 to 3.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | > 200 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | > 160 | °C | ISO 75-2/C |
| CLTE - Flow (50 to 150°C) | 1.5E-5 to 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.70 to 0.90 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 to 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 to 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 20 to 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 6.00 4.00 | ||
| 1 MHz | 6.00 4.00 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 to 0.020 | ||
| 1 MHz | 0.020 to 0.040 | ||
| Arc Resistance | PLC 4 | ASTM D495 | |
| Comparative Tracking Index | > 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 900 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 900 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Middle Temperature | 50.0 to 70.0 | °C | |
| Front Temperature | 70.0 to 90.0 | °C | |
| Processing (Melt) Temp | 90.0 to 105 | °C | |
| Mold Temperature | 150 to 190 | °C | |
| Back Pressure | 0.500 to 1.50 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 168 h / 110°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styropor® P-340A H | BASF Corporation | PS (EPS) | Styropor® |
| Bynel® 4208 | DuPont Packaging & Industrial Polymers | LDPE | Bynel® |
| FHR Polypropylene P4C6Z-059 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| GAPEX® RPP35EC15BK | Ferro Corporation | PP Homopolymer | GAPEX® |
| MAJ'ECO AP404W | AD majoris | PP, Unspecified | MAJ'ECO |