GELOY™ XP4025 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Ll9kPv_GELOYXP4025resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GELOY XP4025 is a high heat modified ASA/PC blend, for automotive exterior applications. It shows very good properties, gloss and colour retention, as well as faster cycle time over competitive material. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 220°C/10.0 kg | 5.00 | cm³/10min | ISO 1133 |
| 260°C/5.0 kg | 18.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.70 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 98.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 50.0 | MPa | ISO 527-2/5 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Fracture | 40.0 | MPa | ISO 527-2/5 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/5, ISO 527-2/50 | ||
| Yield | 4.0 | % | ISO 527-2/5, ISO 527-2/50 |
| Fracture | 15 | % | ISO 527-2/5, ISO 527-2/50 |
| Flexural Modulus 2 | 2350 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 140 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 5 | ISO 180/1A | ||
| -40°C | 6.0 | kJ/m² | ISO 180/1A |
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| -10°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 100 mm span | 104 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 86.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 104 | °C | ISO 306/B50 |
| -- | 107 | °C | ISO 306/B120 |
| Ball Pressure Test (75°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.24 | W/m/K | ISO 8302 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.20 mm, in Oil) | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 4.30 | IEC 60250 | |
| 60 Hz | 4.30 | IEC 60250 | |
| 1 MHz | 3.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 0.18 | IEC 60250 | |
| 60 Hz | 0.18 | IEC 60250 | |
| 1 MHz | 0.021 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 225 | V | IEC 60112 |
| Solution B | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 220 - 250 | °C | |
| Middle Temperature | 230 - 260 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Nozzle Temperature | 230 - 260 | °C | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 50.0 - 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcobond® W-296 | Chemtura | PUR-Ester | Witcobond® |
| Unichem 8083 | Colorite Polymers | PVC, Unspecified | Unichem |
| KPOL-HDPE HD K-20/960 | KPOL Chem Co. | HDPE | KPOL-HDPE |
| Exceed™ 3812CB | ExxonMobil Chemical | mPE | Exceed™ |
| OTECH TPE OTR6988 - Profile | OTECH Corporation | TPE | OTECH TPE |