Advanced-PP 1102LQ
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Advanced Petrochemical Company |
| Trademark: | Advanced-PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LkNyXU_Advanced-PP-1102LQ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Advanced-PP 1102LQ is a propylene homopolymer with narrow MFR and general extrusion additivation. It is specificially designed for stretched tape yarn, carpet backing and artificial grass. Also suited for Raffia & Thermoforming Applications. Application Thermoformed Parts, Raffia, Carpet backing & General Extrusion. Regulatory Information: The Grade Advanced-PP 1102LQ and additives incorporated comply with United States FDA Regulation 21CFR 177.1520 Olefin Polymers and European Regulation (EU) 10/2011. Specific information is available upon request. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 74.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 9.0 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 140 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength (23°C) | 3.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 154 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MNF 2510 H | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| TECOLITE KM-13B(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| Wellamid® MRGF1647-BK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| XYLEX™ X8409AC resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |
| TABOREN® PC 23 T 25-973 | SILON s.r.o. | PP Copolymer | TABOREN® |