LNP™ THERMOCOMP™ MFB22J compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LgzMLA_LNP-THERMOCOMP-MFB22J-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* THERMOCOMP* MFB22J is a compound based on Polypropylene resin containing Glass Bead and Glass Fiber. Added feature of this material is: Low Extractable. Also known as: LNP* THERMOCOMP* Compound MFB22J Product reorder name: MFB22J |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3950 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 34.0 | MPa | |
| Break | 25.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 3.2 | % | |
| Break | 6.3 | % | |
| Flexural Modulus 4(50.0 mm Span) | 3150 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 54.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 108 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Terluran® SP-6 | INEOS Styrolution Group GmbH | ABS | Terluran® |
| VITAMIDE® AK40 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| Capilene® S 89 E | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| Cogegum® GFR/365 | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| Daplen™ EE209AE | Borealis AG | PP, Unspecified | Daplen™ |