Starex WR-9120 J
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LgsuOH_Starex-WR-9120-J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex WR-9120 J is an Acrylonitrile Styrene Acrylate (ASA) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 26 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2000 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 44.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2/50 |
| Break 3 | 39.0 | MPa | ASTM D638 |
| Break | 34.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 85 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 2260 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 64.0 | MPa | ASTM D790 |
| -- 8 | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 3.18 mm) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 91.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 99.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 77.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 94.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 180 to 190 | °C | |
| Middle Temperature | 200 to 210 | °C | |
| Front Temperature | 220 to 230 | °C | |
| Nozzle Temperature | 240 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF D-1 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| TPC PVC SG840 | Thai Plastics and Chemicals Public Company Limited | PVC Homopolymer | TPC PVC |
| BMC 800 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| CompaDur® 121 GF 30 natural (005) | DimeLika Plast GmbH | PBT | CompaDur® |
| Golden Compound PP S²PC 3545BO 40LH41 | Golden Compound GmbH | PP, Unspecified | Golden Compound |