Macromeric® 0103-212a BK
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Saco Polymers |
| Trademark: | Macromeric® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LgPXew_Macromeric-0103-212a-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Black Non-halogen flame retardant compound Macromeric ® 0103-212a BK is a black, UV resistant, non-halogen flame retardant RoHS polyolefin compound. It is designed for use in a wide variety of jacketing applications including wire and cable. This compound has superior fire performance; including slow flame propagation, self-extinguishing characteristics, and low smoke production. Macromeric ® 0103-212a BK should be extruded with a screw configuration designed to optimize process conditions and throughput. This extrusion compound meets, or exceeds, several industry jacketing specifications, including UL 1277 tray cable. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.51 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 3.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec | 93 | ||
| Shore D, 1 sec | 59 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 13.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 180 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 228 | MPa | ASTM D790 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | ASTM D638 | ||
| 121°C, 336 hr | 5.0 | % | |
| 136°C, 168 hr | 5.0 | % | |
| Change in Ultimate Elongation in Air | ASTM D638 | ||
| 121°C, 336 hr | -5.0 | % | |
| 136°C, 168 hr | -10 | % | |
| Change in Tensile Strength (70°C, 4 hr, in Oil) | -15 | % | ASTM D638 |
| Change in Ultimate Elongation (70°C, 4 hr, in Oil) | 5.0 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 2 | -34.0 | °C | ASTM D746 |
| UL Temperature Rating 3 | 90 | °C | UL 1581 |
| Deformation - 2000-gram load (121°C) | 2.5 | % | UL 1277 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 171 to 182 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index 4 | 38 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 149 to 160 | °C | |
| Cylinder Zone 2 Temp. | 166 to 177 | °C | |
| Cylinder Zone 3 Temp. | 177 to 188 | °C | |
| Cylinder Zone 4 Temp. | 177 to 188 | °C | |
| Melt Temperature | 182 to 193 | °C | |
| Die Temperature | 188 to 199 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 3 minutes in methanol |
| 3 . | Test Conditions: Air, 150-days at 97°C |
| 4 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE PCG80 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TOTAL Polyethylene HDPE 7194 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| BCC Resins BC 8990 | BCC Products Inc. | TSU | BCC Resins |
| Karina MBU PINK E 39/338-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupolen 2427 K | LyondellBasell Industries | LDPE | Lupolen |