Heramid® A NER MP/1K
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Heramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LgBnUP_Heramid-A-NER-MP-1K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 injection moulding grade. Toughened, heat stabilizaed. Black colour. Post-industrial grade produced with selected polymers coming from polymerization, fibres and compounding plants. ISO 1043 : PA66-IT |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 53 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 30 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2200 | MPa | ISO 178 |
| Flexural Stress 2 | 85.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 66.0 | °C | ISO 75-2/Af |
| Melting Temperature | 260 | °C | ISO 11357 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 830 | Celanese Corporation | TPC-ET | Riteflex® |
| AFLAS® 300S | Asahi Glass Co., Ltd. | Fluorelastomer | AFLAS® |
| Capilene® T 12 EV | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| RTP 799 X 143524 EG | RTP Company | HDPE | RTP |
| TOTAL Polyethylene Aceso® PEM 2440 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |