Ebalta SG 140 / PUR 12
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LgA2Wl_Ebalta-SG-140-PUR-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This is a Polyurethane system. Material should be carefully stirred up/ shaked before use. Filler content and sales units are on the separate mixing table noted. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 69 to 75 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1270 to 1430 | MPa | ISO 178 |
| Flexural Stress | 40.0 to 50.0 | MPa | ISO 178 |
| Compressive Stress | 30.0 to 40.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 12 to 18 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 43 to 47 | °C | DIN 53458 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 91 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.03 to 1.07 | g/cm³ | |
| Viscosity (25°C) | 0.060 to 0.080 | Pa·s | |
| Curing Time (20°C) | 0.50 to 1.0 | hr | |
| Pot Life 1(20°C) | 4.0 to 5.0 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A GF 10 | A. Schulman Europe | PBT | SCHULADUR® |
| Cellophane™ 340XSC | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Garaflex™ O 9940SA NAT | AlphaGary | TPE | Garaflex™ O |
| LUVOCOM® 1/CF/10/TF/20/GY | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Hifax CA 1210 G 1740 | LyondellBasell Industries | PP Copolymer | Hifax |