| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | The Matrixx Group, Inc. |
| Trademark: | Matrixx |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Lfq6sE_Matrixx-CPP1B10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Matrixx CPP1B10 is a polypropylene material, and its filler is 10% calcium carbonate filler. This product is available in North America and is processed by injection molding. The main characteristics of Matrixx CPP1B10 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.1 - 1.5 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 30.3 | MPa | ASTM D638 |
| Flexural Modulus - Tangent | 1650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 37 | J/m | ASTM D256 |
| Dart Drop Impact | 2.26 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| RTI | 65.6 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 104 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 188 - 232 | °C | |
| Middle Temperature | 188 - 232 | °C | |
| Front Temperature | 188 - 232 | °C | |
| Processing (Melt) Temp | 199 - 232 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.138 - 2.07 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Drying not normally requiredInjection Booster Pressure: Maximum without flash, 60% of machine maximum, targetScrew Speed: Slow to Medium |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tislamid® PA66 PA66 UNR | Tisan | Nylon 66 | Tislamid® PA66 |
| Bormod™ HD915CF | Borealis AG | PP Homopolymer | Bormod™ |
| Elvax® 3190 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Elvax® 250 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| LNP™ LUBRICOMP™ WFL369 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |