INNOPOL® CS 4-8820 is a 20 % glass-fibre filled chemically coupled polypropylene random copolymer compound. This grade is available in nature and custom coloured form. Recommended application INNOPOL® CS 4-8820 is suitable for multilayer pipes. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 62.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 5.0 | % | |
| Break | 7.0 | % | |
| Flexural Modulus 1 | 3700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1e | ||
| -20°C | 9.0 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 9.6 | kJ/m² | |
| 23°C | 17 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 113 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 141 | °C | ISO 306/A120 |
| -- | 104 | °C | ISO 306/B120 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Cylinder Zone 1 Temp. | 180 to 220 | °C | |
| Cylinder Zone 2 Temp. | 180 to 220 | °C | |
| Cylinder Zone 3 Temp. | 180 to 220 | °C | |
| Cylinder Zone 4 Temp. | 180 to 220 | °C | |
| Cylinder Zone 5 Temp. | 180 to 220 | °C | |
| Melt Temperature | 200 to 220 | °C | |
| Die Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| COPYLENE® CH040 | Phillips 66 | PP Homopolymer | COPYLENE® |
| Duratel MF9 | Custom Resins Group | Acetal (POM) Copolymer | Duratel |
| Huafon HF-1395AX | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Latishield 85-08A G/20 | LATI S.p.A. | PESU | Latishield |
| Iupilon® LSH2030 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |