HiFill FR® PC FR IM
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill FR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LehZ2l_HiFillFRPCFRIM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill FR®PC FR IM is a polycarbonate (PC) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 55.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 90 | % | ASTM D638 |
| Flexural Modulus | 228 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 116 | °C | ASTM D648 |
| CLTE - Flow | 6.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 17 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.0 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 282 - 293 | °C | |
| Processing (Melt) Temp | 266 - 293 | °C | |
| Mold Temperature | 82 - 121 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 7500N-FM | TSRC Corporation | SEBS | T-Blend® |
| CYROLITE® Protect G23P | Evonik Cyro LLC | Acrylic (PMMA) | CYROLITE® |
| Karina GRAY PVC COMPOUND -E 853-18/ 48-DY-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ QF007 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ THERMOCOMP™ |
| LITEN BB 29 F | Unipetrol RPA, s.r.o. | PE Copolymer | LITEN® |