Resirene HH 103
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Resirene, S.A. de C.V. |
| Trademark: | Resirene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Leahqg_Resirene-HH-103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resirene HH 103 is a GPPS with high molecular weight that shows a high thermal resistance and excellent mechanical resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 2.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ASTM D638 |
| Tensile Strength (Break) | 46.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (12.7 mm) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 90.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 to 190 | °C | |
| Cylinder Zone 2 Temp. | 190 to 200 | °C | |
| Cylinder Zone 3 Temp. | 200 to 210 | °C | |
| Cylinder Zone 4 Temp. | 210 to 220 | °C | |
| Cylinder Zone 5 Temp. | 220 to 230 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Biomer® P300 | Biomer | Biodeg Polymers | Biomer® |
| Exxtral™ Performance Polyolefin CNK010 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Formolene® 6335N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Sylvin 9302-70FU White 1362 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ LUBRICOMP™ RCL36S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |