Xuchuan A-7050/B-6220
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LeTbVF_Xuchuan-A-7050-B-6220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Xuchuan A-7050/B-6220 is a Thermoplastic Polyurethane Elastomer (Polyester) (TPU-Polyester) product. It is available in Asia Pacific. Typical application: Consumer Goods. Primary characteristic: low temperature resistant. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.400 to 0.550 | g/cm³ | |
| Density | |||
| A-7050 : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-6220 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-7050 : 40°C | 1.00 to 1.40 | Pa·s | |
| B-6220 : 40°C | 0.700 to 1.10 | Pa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Ross Flex (-20°C) 1 | No Crack |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 8.0 to 10.0 | sec | |
| End of Rise Time | 50.0 to 60.0 | sec |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 200 to 250 | kg/m³ | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 50 to 60 | °C | |
| Preheat Time | |||
| Part A | 6.0 to 8.0 | hr | |
| Part B | 8.0 to 12.0 | hr | |
| Processing Temperature | |||
| Part A | 40 to 45 | °C | |
| Part B | 38 to 42 | °C |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 45 to 65 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 4.00 to 5.50 | MPa | |
| Tensile Elongation (Break) | 520 to 650 | % | |
| Tear Strength | 16.0 to 26.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 68 to 70 | ||
| Demold Time | 5.0 to 7.0 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 45.0 to 55.0 | °C |
| Note Message | |
|---|---|
| 1 . | 40000 cycles, Break length 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP5032 | PolyMirae | PP Homopolymer | Moplen |
| COSMOPLENE® FC9413G | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP Random Copolymer | COSMOPLENE® |
| ESTYRENICS 123 | PCC Plastics & Consultations Center | PS (GPPS) | ESTYRENICS |
| Dynaprene® 1055A | Nantex Industry Co., Ltd. | TPE | Dynaprene® |
| Karina BLACK PVC COMP. -E 753D48/ 1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |